SURFACE TREATMENT AND EXAMINATION OF GRADE 2 AND GRADE 5 TITANIUM
AbstractSurface characteristics play an important role in the implant-bone integration that is required for the long-term reliability of dental and orthopedic implants. In this paper, we investigate the effect of acid etching on the mass reduction and roughness of grade 2 and grade 5 Ti under controlled experimental conditions. Three different etching compounds were investigated: 30% HCl, 85% H3PO4 and the compound of 30% (COOH)2 × 2H2O and 30% H2O2 in various treatment intervals under controlled temperature. Stereo microscopy, scanning electron microscopy, roughness and weight measurements were carried out on the samples. We found that neither 85% H3PO4 nor the compound of 30% (COOH)2 × 2H2O and 30% H2O2 were able to remove the machining marks from the surface of Ti discs in our experimental setting. On the other hand, etching in 30% HCl yielded even surfaces both on Ti grade 2 and 5 discs. We also found that etching at higher temperatures in 30% HCl resulted in significant mass loss.
Authors who publish with this journal agree to the following terms:
1. Authors retain copyright and grant the journal the right of the first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal.
2. Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., to post it to an institutional repository or to publish it in a book), with an acknowledgement of its initial publication in this journal.
3. Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges as well as earlier and greater citation of the published work (See The Effect of Open Access).